:: Krisow Performance Fluids Inc. ::

ANDEROL® FGCS 2

ANDEROL FGCS 2 is an over-based Calcium Sulfonate based grease with exceptional load carrying ability, excellent mechanical stability and good resistance to oxidation and corrosion.

ANDEROL FGCS 2 equals or outperforms other premium Food-Grade greases.

APPLICATIONS / ADVANTAGES

Superior mechanical stability, particularly in the presence of heat and water

formulated to resist separation under centrifugal forces

Excellent rust prevention properties

Excellent load carrying ability and wear protection

Excellent resistance to water washout and spray-off

H1 grease for incidental contact with food

Heavy duty food-grade applications

Life performance is typically increased by two to three that of a regular mineral oil based grease

REGISTRATIONS / APPROVAL

ANDEROL lubricants are approved, recommended and field tested by many OEM’s in the Food processing, bottling, canning, meat processing and pharmaceutical industries.

HANDLING AND STORAGE

ANDEROL lubricants generally present little hazard in normal handling if ordinary care is exercised. If spilled, cover with inert, absorbent material and remove. Flush the area with water.

Although ANDEROL lubricants are not highly flammable, they will burn and should be kept away from open flames. In case of fire, use water spray, foam, carbon dioxide, or dry chemical.

ANDEROL lubricants should be stored preferably in protected locations to prevent contamination. Do not re-use drums; flush and send to re-conditioner.

PROPERTIES	TEST METHOD	ANDEROL FGCS 2
Thickener	-	Ca-Sulfonate
Color	-	Tan
Type of Base Oil	-	White Oil
Operating temperature for long-term lubrication, °C	-	-20 to 160 °C
Short term admissible temperature peak value, °C	-	+200°C
Dropping Point, °C	DIN ISO 2176	318°C
Worked Penetration	DIN ISO 2137	265 to 295 0.1 mm
Base Oil Viscosity at 40°C	DIN 51.562	Approx. 95 mm²/s
4-Ball Weld Load	ASTM D-2596	4000 N
Water Washout @ 80°C	ASTM D-1264	0.3% removed
Bearing Life Performance, hours @ 1000 rpm, 160°C	ASTM D-3527	180 hours
Low Temperature Torque at -40°C	ASTM-D-4693	11.0 Nm
Designation	DIN 51.502	KP 2 U-40